The High Frequency Reciprocating Rig (HFRR) is a microprocessor-controlled reciprocating friction and wear test system which provides a fast, repeatable assessment of the performance of fuels and lubricants. It is particularly suitable for wear testing relatively poor lubricants such as diesel fuels and for boundary friction measurements of engine oils, greases and other compounds. It has become the industry standard test for diesel fuel lubricity and conforms to ASTM D6079, ASTM D7688, CEC F-06-A, ISO 12156, EN 590, JPI-5S-50 and IP 450.The High Frequency Reciprocating Rig (HFRR) is a microprocessor-controlled reciprocating friction and wear test system which provides a fast, repeatable assessment of the performance of fuels and lubricants. It is particularly suitable for wear testing relatively poor lubricants such as diesel fuels and for boundary friction measurements of engine oils, greases and other compounds. It has become the industry standard test for diesel fuel lubricity and conforms to ASTM D6079, ASTM D7688, CEC F-06-A, ISO 12156, EN 590, JPI-5S-50 and IP 450.

Consumable Description

•HFRR standard specimens are sold as a pack of 100 upper and 100 lower specimens. The upper specimen is a 6mm diameter ball that is loaded into the upper specimen holder and the lower specimen is a 10mm disc that is loaded into the lower specimen holder.

•Standard Specimen Pack – Part code: HFRSSP

•This standard specimen pack comprises 100 upper and 100 lower specimens for use in the HFRR and are manufactured to comply with ISO and ASTM standards.

•Upper Specimen (Ball)

•The upper specimen is specified to grade 28 (ANSI B3.12), ANSI E-52100 steel, with a Rockwell hardness “C” scale (HRC) number of 58-66 (ISO 6508), and a surface finish of less than 0.05 µm Ra.

•Lower Specimen (Disc)

•The lower specimen is specified to AISI E-52100 steel machined from annealed rod, with Vickers hardness “HV30” scale number of 190-210 (ISO 6507/1). It is turned, lapped and polished to a surface finish of less than 0.02µm Ra.

HFRR standard specimens are sold as a pack of 100 upper and 100 lower specimens. The upper specimen is a 6mm diameter ball that is loaded into the upper specimen holder and the lower specimen is a 10mm disc that is loaded into the lower specimen holder.

Standard Specimen Pack – Part code: HFRSSP

This standard specimen pack comprises 100 upper and 100 lower specimens for use in the HFRR and are manufactured to comply with ISO and ASTM standards.

Upper Specimen (Ball)

The upper specimen is specified to grade 28 (ANSI B3.12), ANSI E-52100 steel, with a Rockwell hardness “C” scale (HRC) number of 58-66 (ISO 6508), and a surface finish of less than 0.05 µm Ra.

Lower Specimen (Disc)

The lower specimen is specified to AISI E-52100 steel machined from annealed rod, with Vickers hardness “HV30” scale number of 190-210 (ISO 6507/1). It is turned, lapped and polished to a surface finish of less than 0.02µm Ra.

HFRR standard specimens are sold as a pack of 100 upper and 100 lower specimens. The upper specimen is a 6mm diameter ball that is loaded into the upper specimen holder and the lower specimen is a 10mm disc that is loaded into the lower specimen holder.

Standard Specimen Pack – Part code: HFRSSP

This standard specimen pack comprises 100 upper and 100 lower specimens for use in the HFRR and are manufactured to comply with ISO and ASTM standards.

Upper Specimen (Ball)

The upper specimen is specified to grade 28 (ANSI B3.12), ANSI E-52100 steel, with a Rockwell hardness “C” scale (HRC) number of 58-66 (ISO 6508), and a surface finish of less than 0.05 µm Ra.

Lower Specimen (Disc)

The lower specimen is specified to AISI E-52100 steel machined from annealed rod, with Vickers hardness “HV30” scale number of 190-210 (ISO 6507/1). It is turned, lapped and polished to a surface finish of less than 0.02µm Ra.

HFRR standard specimens are sold as a pack of 100 upper and 100 lower specimens. The upper specimen is a 6mm diameter ball that is loaded into the upper specimen holder and the lower specimen is a 10mm disc that is loaded into the lower specimen holder.

Standard Specimen Pack – Part code: HFRSSP

This standard specimen pack comprises 100 upper and 100 lower specimens for use in the HFRR and are manufactured to comply with ISO and ASTM standards.

Upper Specimen (Ball)

The upper specimen is specified to grade 28 (ANSI B3.12), ANSI E-52100 steel, with a Rockwell hardness “C” scale (HRC) number of 58-66 (ISO 6508), and a surface finish of less than 0.05 µm Ra.

Lower Specimen (Disc)

The lower specimen is specified to AISI E-52100 steel machined from annealed rod, with Vickers hardness “HV30” scale number of 190-210 (ISO 6507/1). It is turned, lapped and polished to a surface finish of less than 0.02µm Ra.

HFRR standard specimens are sold as a pack of 100 upper and 100 lower specimens. The upper specimen is a 6mm diameter ball that is loaded into the upper specimen holder and the lower specimen is a 10mm disc that is loaded into the lower specimen holder.

Standard Specimen Pack – Part code: HFRSSP